Heat Treatment is the controlled heating and cooling of metals to alter their physical and mechanical properties without changing the product shape. Heat treatment is sometimes done inadvertently due to manufacturing processes that either heat or cool the metal such as welding or forming. Heat Treatment is often associated with increasing the strength of material, but it can also be used to alter certain manufacturability objectives such as improve machining, improve formability, restore ductility after a cold working operation. Thus it is a very enabling manufacturing process that can not only help other manufacturing process, but can also improve product performance by increasing strength or other desirable characteristics.

Category: Engineering

23 Terms

Created by: Naveed

Number of Blossarys: 5

My Terms

Collected Terms

Terms

Newest on top

Terminite tõlkimine

Add a term

Estonian (ET)

Compare Language

Normalizing

Normalizing is a process of heating steel to about 40 to 50 degree above upper critical temperature,holding for proper time,and then cooling in still air or at room temperature.

Spheroidizing

Spheroidizing is a heat treatment process which results in a structure consisting of globules or spheroids of carbide in matrix of ferrite.

Process Annealing

In this treatment,steel is heated to a temperature below the lower critical temperature,and is held at this temperature for sufficient time and then cooled.

Recrystallization Annealing

Practically all steels,which have been heavily cold worked,are subjected to this treatment.The process consists of heating steel above the recrystallization temperature and cooling thereafter.

Partial Annealing

Partial annealing is also referred to as interstitial annealing or incomplete annealing.In this process,steel is heated between the lower critical temperature and the upper critical temperature.

Diffusion Annealing

The process,also known as homogenizing annealing,is employed to remove any structural non uniformity.In diffusion annealing treatment,steel is heated sufficiently above the upper critical ...

Isothermal Annealing

In this process,hypoeutectoid steel is heated above the upper critical temperature and held for some time at this temperature.This is done in order to get a completely austenitic structure and to ...